I have several 12-14” wet maple bowl blanks. I have always twice turned bowls, but want to try once turned. What is a good thickness for these size bowls? Should the rim just be plain or can you add some type of embellishment?
Thanks for the explanation. I did a live oak once turned a few years ago and got that effect but did not know what caused it.1/4" to 3/8" thickness works well for me on once turned bowls. Sometimes thicker for large natural edge bowls, especially if they have an unusual rim shape (from a tree with weird outer shape.)
Keep in mind that the shape of the bowl changes and is no longer round when it's dry.
With the thinner bowls, coring can be a more fruitful. I like making cut rim bowls from blanks in the natural edge orientation. It's possible to get 2 or even 3 bowls of very similar and useable size from the same blank.
- For natural edge bowls, this can add to the appeal. But it can detract too. Some shapes that look good off the lathe don't look good once dry. For me, NE bowls that have retreat curve (correct term?) where the diameter at the rim is less than than the diameter further down, look worse when dry.
- For cut rim bowls, the rim will not be flat. If the rim of the bowl is from the pith side of the blank, you might end up with a pronounced peak on the dry bowl near the pith location. To me the cut rims look much better when they are from the bark side of the blank, (same orientation you would use for a natural edge bowl). Then the rim un-evenness is more gradual and less noticeable. I also prefer the grain pattern - ovals in the bottom of the bowl - from the natural edge orientation.
With once turned bowls, you can get cool surface texture with figured wood, like crotch pieces or curl. The figured spots don't shrink as much as the adjacent, unfigured wood. So if you sand the surface before the bowl is dry (have to do it soon, since thin bowls dry fast), the dry bowl will have an uneven, corduroy like surface. This can be positive or negative, depending on the effect you are after.
It's more difficult to sand a warped, once turned bowl than a round twice turned bowl. Work hard to get a good surface with minimal tool marks. If my schedule allows, I like to sand the bowls the day after I cut them. After spending the night in a paper bag, the surface is dry enough so that it doesn't gum up sandpaper, but the bowl is wet enough to still be round.
In boatbuilding the term for this is “tumblehome.” I don’t know if there’s a term for it in turning.NE bowls that have retreat curve (correct term?) where the diameter at the rim is less than than the diameter further down, look worse when dry.
What is a kraft type grocery bag?Depends on intended use. For display only, down to 1/8” wall, leave bark or not. Bowl to be used/handled, 1/4-3/8”, no bark, it will break off when the bowl is handled.
As discussed rims will warp from drying. IMO most embellishments dont look that great on a thin rim, and a wide rim stands a good chance of cracking, and the embellishments can get pretty twisted.
I sand when dry, mounted on the lathe, with a drill at low rpm, and turn the piece slowly by hand. Ive tried some sanding while wet, didnt go so great, probably need to try again.
I put all of my wet turnings in double kraft type thick grocery bags and keep them on a wire rack in the house, in constant humidity and temp. Weight as bagged and write it on the bag. Stops losing wt its ready. No mold problems, double bag sows dryinng, less warp and cracking.
The thinner you go, the more important this is - work the ID down in sections, an 1-2 inches at a time, you cant go back up toward the rim, its moved.
What is a kraft type grocery bag?
Example: BagDream Grocery Bags 12x7x17 Inches 100Pcs Heavy Duty Kraft Brown Paper Grocery Bags Durable Kraft Paper Bags, Paper Barrel Sack Bags, 100% Recycled Kraft Paper Gift Bags Bulk https://www.amazon.com/dp/B07Q2XWN5...t_i_4F46R7NGV659ZMWZ17B1?_encoding=UTF8&psc=1Brown paper....thick
Ah, thanks. Those pqper bags are just starting to come into stores around here.Example: BagDream Grocery Bags 12x7x17 Inches 100Pcs Heavy Duty Kraft Brown Paper Grocery Bags Durable Kraft Paper Bags, Paper Barrel Sack Bags, 100% Recycled Kraft Paper Gift Bags Bulk https://www.amazon.com/dp/B07Q2XWN5...t_i_4F46R7NGV659ZMWZ17B1?_encoding=UTF8&psc=1
I reuse them numerous times.
Large bowls, platters, etc that dont fit a bag:
Builder's paper Paper 3-ft x 140-ft Drop Cloth https://www.lowes.com/pd/Blue-Hawk-Builder-s-Paper-1-Pack-Paper-3-ft-x-140-ft-Drop-Cloth/50265367
Painters tape to close them.
I would suggest that a paper bag would be a better choice or no bag at all. Correction I was thinking that the bag used was plastic.Thanks for all the information . I turned the bowl yesterday to around 5/16” thick, weighed it and put in a lawn and leaf bag overnight. No cracks this morning. I turned it the same as a natural edge (from the bark side). It is warping, diameter now is 11 7/8” X 11 1/8”. I’ll keep it in. the bag for about a week and then let air dry.
View attachment 42632View attachment 42633
Most lawn/leaf bags are paper. We have to use paper bags for lawn/yard trash.I would suggest that a paper bag would be a better choice or no bag at all. Correction I was thinking that the bag used was plastic.
It is a paper lawn and leaf bag.I would suggest that a paper bag would be a better choice or no bag at all. Correction I was thinking that the bag used was plastic.
Wait and seeIt is a paper lawn and leaf bag.
That leads to a final question. I expect you “flatten the bottom once it has dried, correct?
As far as the lawn and leaf bags are concerned I moved out of the city in 2006 at that time I believe that the bags were plastic but I now don't have any need to bag I just throw the leaves back in the uncleared woods.It is a paper lawn and leaf bag.
That leads to a final question. I expect you “flatten the bottom once it has dried, correct?
I have about a 1/4-5/16” thickness. Not knowing I turned a very shallow recess initially. I could either try and true up the recess or sand it round.Wait and see
Round bottoms are surprisingly stable. Especially when the bottom is centered on the grain
I leave round bottoms on most of by NE bowls and HFs.
The bottom grain in your bowl is off center - inch??
So your bowl might sit a more bit tilted than if it were centered. Probably will look just fine
The warp centers around the growth rings.
If you like the way it looks on its bottom the warp chose then done.
If you want it to sit on another spot you need to turn a recess- Do you have enough thickness ?https://www.aawforum.org/community/...]=18856&hash=2677f3f0cc405030b9c3ade6ee04920b
I removed the tenon already and put a small foot on the bowl when I turned the bowl. I held it with my vacuum chuck. I may have to round the bottom as not a lot of thickness to work with or just leave it as is.As far as the lawn and leaf bags are concerned I moved out of the city in 2006 at that time I believe that the bags were plastic but I now don't have any need to bag I just throw the leaves back in the uncleared woods.
The bottom can be flattened when the tenon is removed or if you used a a recess you still may want to jam chuck it to true or remove the the recess. The trued up recess can be used to hold the bowl for spray finishing, which allows heaver coats when it is slowly rotated.
have about a 1/4-5/16” thickness. Not knowing I turned a very shallow recess initially. I could either try and true up the recess or sand it round.
William like I have been saying, yes dry the green bowl in a brown paper bag, I've always used the bags from places like KFC, as these are good bags also from other like sources.Thanks for all the information . I turned the bowl yesterday to around 5/16” thick, weighed it and put in a lawn and leaf bag overnight. No cracks this morning. I turned it the same as a natural edge (from the bark side). It is warping, diameter now is 11 7/8” X 11 1/8”. I’ll keep it in. the bag for about a week and then let air dry.
View attachment 42632View attachment 42633
Leo, that first picture shows more bowls than I have turned. You really get after it. Looks like some in the second picture have sealer on the end grain. Correct?William like I have been saying, yes dry the green bowl in a brown paper bag, I've always used the bags from places like KFC, as these are good bags also from other like sources.
I do not like the leaf bags bags for the reason that these have the inner bag sealed with tar between the layers, so he absorbing and releasing of the paper isn't going to happen, as for length of time. it depends a lot on the thickness of the bowl's wall and foot, here are a couple pictures that show how I have been doing this and still do.
Here are some Ash bowls that have just been taken out of the brown paper bags.
View attachment 42635
Here I just checked the bowls to see if they are dry enough to take them out of the bag for further drying.
View attachment 42636
These bowls are dry and can be returned when I have time.
View attachment 42637
I did that when I was younger. Probably the cause of my tinnitusOr you can choose to let it rock a little bit…
That leads to a final question. I expect you “flatten the bottom once it has dried, correct?
That is the most common way to do it but there are 2 notes for this process, #1 the area of the foot can safely be left thicker due to the flat long grain and # 2 the last step in working the base is to cut a cone from the live center to the bowl, then if the grain is straight just break it off and sand the center until all traces of it are gone.I put a simple, small foot on once turned bowls, similar to what I do for twice turned bowls.
The key difference is that the foot becomes oval and unflat as the bowl dries. Once the bowl is dry, I mount it using a friction drive, aka jam chuck, cut the bottom flat and cut a recess on the inside. So the center of the foot is round, the outside of the foot is oval. (See picture; the flats on the ends of the foot are wider than on the sides). I've tried making the outside of the foot round, but it's hard to make the transition back to warped sides of the bowl, at least for large bowls. .
View attachment 42648
Here's a picture of the completed (no finish yet) bowl, showing the foot:
View attachment 42649
No sealer on any of the rough turned bowls William, there is CA on spots like knots or what I know could become problem spots.Leo, that first picture shows more bowls than I have turned. You really get after it. Looks like some in the second picture have sealer on the end grain. Correct?
The lawn and leaf bags I have seem to be just paper, cheap ones.
Reed these are not 3 or 4 mm thick Arbutus bowls that you have to turn that thin or else they will split, you have the experience there, however the real problem with these other wood species of bowls, and turned a bit thicker, here comes the big difference in the speed of the engrain drying and the side grain drying to play its roll, that is where the tension comes from, and unless the wall can accommodate this by warping without splitting, it will split.I don't know if you can even find them any more, but feed sack bags used to be several layer thick brown craft paper. It worked well, or at least better than single thickness grocery bags. With the once turned bowls, it seldom is necessary to wrap them. The vulnerable point on a bowl when drying is the rim. Rounding over the rim is done for safety so you don't slice yourself, and also the rounded edge is less prone to cracking than a sharp edge where the sharp part dries first = stress = cracking. I found the stretch film to be a big help in protecting the rim. Knots and pith are also crack instigators.....
robo hippy